主要成份：陶瓷微粉、树脂等。
产品描述：本产品为双组份材料，A组份为主剂，外观为白色膏状；B组份为固化剂，外观为浅黄色液体。A、B组份按比例混合后常温固化，固化后的材料具有优良的粘接性能。
用 途：作为施卓®的碳化硅耐磨防护剂的底剂，增强碳化硅耐磨涂层与基材的粘接力。
优 点：常温固化，普遍适用于金属、陶瓷、石材、混凝土、橡胶、木材等基材。
Main Ingredients: Ceramic micro-powder, resin, etc.
Product Description:This product is a two-component material. Component A is the base agent, appearing as a white paste, while Component B is the curing agent, presenting as a pale yellow liquid. When mixed in the specified ratio, the components cure at room temperature. The cured material exhibits excellent bonding properties.
Application:Used as the primer for SYZO® Silicon Carbide Wear-Resistant Protective Coating, enhancing the adhesion between the silicon carbide wear-resistant layer and the substrate.
Advantages: Cures at room temperature and is widely applicable to various substrates such as metal, ceramic, stone, concrete, rubber, wood, etc.
包装规格：
施工步骤：
1、对待修复设备进行喷砂或打磨，使设备表面粗糙化；
2、对设备表面进行清洗，做到表面无水、无油、无尘；
3、混合A、B组份，并施涂在待修复设备表面。
Construction Steps:
1.Perform sandblasting or grinding on the equipment to be repaired to roughen the surface.
2.Clean the equipment surface to ensure it is free of water, oil, and dust.
3.Mix components A and B, then apply the mixture to the surface of the equipment to be repaired.
安全须知：
• 须在通风良好的环境中进行，必须穿戴工作服、口罩、手套、防护眼镜；
• 施工时应避免皮肤直接接触材料。
Safety Precautions:
• Must be used in a well-ventilated environment.
• Wear protective workwear, a mask, gloves, and safety goggles at all times.
• Avoid direct skin contact with the material during application.
注意事项：
• 如长时间存放后，A组份的底部可能会有一些软沉淀，属于正常现象，请用搅拌棒将A组份搅拌均匀后再使用；
• 一般情况下，1套底剂合适1平方米左右的施工。但基材表面比较粗糙或孔洞较多时，用料量将会增加；
• 冬季施工时，温度较低，底剂的A组份会比较粘稠，可以将A组份加热到40℃-50℃后，再加入B组份混合后使用，这样将更便于刷涂。
Precautions:
• If stored for an extended period, some soft sediment may settle at the bottom of Component A. This is normal—stir Component A thoroughly with a mixing rod before use.
• Generally, one set of primer is suitable for approximately 1 square meter of application. However, material consumption will increase if the substrate surface is rough or porous.
• During winter construction, low temperatures may cause Component A to become more viscous. For easier brushing, heat Component A to 40°C–50°C before mixing with Component B.